Effect of Dy2O3 on the phase formation and electrical properties of Tl-1223 HTS

Abstract

TlBa2Ca2Cu3DyxO8+δ superconductor samples (x = 0–0.075) were prepared by a two-step solid-state reaction technique to investigate the impact of Dy2O3 (dysprosium sesquioxide) addition on the formation and the transport properties of the Tl-1223 phase. The samples were analyzed using X-ray powder diffraction, AC susceptibility, and high-harmonics temperature dependence to study the effects of Dy2O3 on phase formation, superconducting transition temperature Tc, and the intergrain critical current density Jc. XRD results revealed that the prepared samples are nearly single-phases Tl-1223 with a tetragonal structure. Tc is not suppressed as Dy content increased, while Jc increased up to x = 0.025, then decreased with a further increase in x. Our findings show that the presence of dysprosium sesquioxide promotes the high-Tc phase and enhances the transport critical current densities.